Simple Diffusion Dependent Transformations
No change in number or composition of phases present
Diffusion Dependent Transformations
Alterations in phase compositions and number of phases present
Diffusionless Transformations
metasta...
MATSE 259 - Exam 3 Questions With Verified
Solutions
Simple Diffusion Dependent Transformations
No change in number or composition of phases present
Diffusion Dependent Transformations
Alterations in phase compositions and number of phases present
Diffusionless Transformations
metastable phase, diffusion is very slow, a new phase
Two Types of Phase Transformation Stages
Nucleation (small particles) & Growth (increasing the size, parent phase disappears)
Two Types of Nucleation
Homogenous (uniform throughout parent phase) & Heterogenous (structural irregularities, container
surfaces and insoluble impurities)
What is the rate of transformation?
1/t(0.5)
Phase Transformations
1. crossing boundary in phase diagrams
2. during transformation - alloy proceeds to equilibrium
3. but most take time - heat treatment and microstructure
4. in reality we cool rapidly and get intermediate phases
Pearlite
1. austenite to alpha + Fe3C
2. Higher temp- coarse pearlite Lower temp- fine pearlite
Bainite
1. diffusion is involved
2. appear like plates and needles
3. thickness depends on temp
4. after nose on diagram
If some portion forms into pearlite or kainite, what must happen before transforming into another
microconstutuent?
Must reheat back to Austenite
Spheroidite
1. heating pearlite or bainite just below eutectoid for long period (24 hr)
2. Fe3C spheres
, Martensite
1. rapidly cooling to very low temperatures
2. not enough time for diffusion (diffusionless)
3. Cools without passing through transformation curves
4. Body Centered tetragonal (supersaturated, transform into another structure, diffusionless)
5. Appears of sharp plates and needles,
6. Retain Austenite can exist
7. DOES Not appear on phase diagram
Alloy Steels
1. Plain Steel - If carbon is only alloying element
2. Alloy Steel - If you add Cr, Ni, Si, or Mn
3. They shift isothermal curve and delay
Continous Cooling Diagrams
1. Time is required for reaction to begin and end
2. Isothermal curves are shifted to larger time and lower temps
Critical Cooling Rate
The minimum rate of quench that produces totally martensite structure
How to Increase Mechanical Behavior?
1. Increase carbon content (more Fe3C, stronger, yield and UTS)
Rank the microstructures that can be produced by quenching the eutectoid of Austenite
Martensite
Tempered Martensite
Fine Bainite
Coarse Bainite
Fine Pearlite
Coarse Pearlite
Spheroidite
Tempered Martensite
1. martensite after quenching is very brittle
2. increase in ductility and toughness by tempering
3. Almost as hard/strong as martensite but better ductility
4. If over tempered, becomes spheroidic
Temper Embrittlement
1. when impact test shows a reduction in toughness of the tempered steel
2. occurs when steel tempered @ 1070 & slow cooled or steel tempered from 700-1070 and found in
concentrations of Ni or Mg
3. result is duc to brit transition temp is shifted higher
4. crack propagation - intergranular (along GB)
5.Control by: compositional control OR tempering >1070 or <700 before quenching to room temp
Austenite Tree
Slow Cooled: Pearlite
The benefits of buying summaries with Stuvia:
Guaranteed quality through customer reviews
Stuvia customers have reviewed more than 700,000 summaries. This how you know that you are buying the best documents.
Quick and easy check-out
You can quickly pay through credit card or Stuvia-credit for the summaries. There is no membership needed.
Focus on what matters
Your fellow students write the study notes themselves, which is why the documents are always reliable and up-to-date. This ensures you quickly get to the core!
Frequently asked questions
What do I get when I buy this document?
You get a PDF, available immediately after your purchase. The purchased document is accessible anytime, anywhere and indefinitely through your profile.
Satisfaction guarantee: how does it work?
Our satisfaction guarantee ensures that you always find a study document that suits you well. You fill out a form, and our customer service team takes care of the rest.
Who am I buying these notes from?
Stuvia is a marketplace, so you are not buying this document from us, but from seller ACADEMICAIDSTORE. Stuvia facilitates payment to the seller.
Will I be stuck with a subscription?
No, you only buy these notes for $10.59. You're not tied to anything after your purchase.