isothermal Correct Answer: TTT curve is an ____________ transformation
coarse pearlite Correct Answer: occurs at temperatures just below eutectoid
(727°C), consists of thick layers, and has higher diffusion rates and slower cooling
rates
fine pearlite Correct Answer: occurs at temperatures around 540°C, consists of
thin layers, and has lower diffusion rates and moderately rapid cooling rates
longer Correct Answer: coarse pearlite has _______ lamellae
shorter Correct Answer: fine pearlite has _______ lamellae
proeutectoid Correct Answer: above and below the eutectoid temperature, a
_____________ phase occurs
bainite, spheroidite, and martensite Correct Answer: other micro-constituents
besides pearlite
bainite Correct Answer: this micro-constituent forms at temperatures below
pearlite
spheroidite Correct Answer: forms when a pearlitic or bainitic microstructure is
held at temperatures below eutectoid for 18 to 24 hours
carbon diffusion Correct Answer: _________ ___________ occurs with
spheroidite, but no change in composition occurs
martensite Correct Answer: micro-constituent that forms when austenite is rapidly
cooled (quenched) at relatively low temperatures
diffusionless; thermal Correct Answer: martensite formation is a _____________
and __________ transformation
BCT (body-centered tetragonal) Correct Answer: structure of martensite
,critical quenching rate Correct Answer: minimum cooling rate required to produce
a completely martensitic microstructure
bainite Correct Answer: with moderate cooling, austenite forms...
martensite Correct Answer: with rapid cooling (quenching), austenite forms...
tempered martensite Correct Answer: when martensite is reheated, it forms...
hard and brittle Correct Answer: quenched condition of martensite is...
below Correct Answer: heat treatment for tempered martensite is ______ eutectoid
temperature
ductility; toughness Correct Answer: relieving internal stresses in tempered
martensite via heat treatment increases __________ and _____________
250 to 650°C Correct Answer: temperature range for tempered martensite
fine Correct Answer: with larger carbon content, _______ pearlite has a higher
Brinell hardness number
coarse Correct Answer: with larger carbon content, _______ pearlite has larger
ductility
harder; stronger Correct Answer: bainite is __________ and __________ than
pearlite
martensite Correct Answer: ________________ is the hardest, strongest, and most
brittle steel microstructure
annealing, stress relief, normalizing, austenitizing, and spheroidizing Correct
Answer: different types of heat treatments
, annealing Correct Answer: a generic term used to denote heat treatment in which
the microstructure and, consequently, the properties of a material are altered;
previously cold-worked material is softened by recrystallization
annealing Correct Answer: heat treatment where material is exposed to an
elevated temperature for extended period of time then slowly cooled
softness; specific Correct Answer: annealing relieves stress, increases
________________, ductility, and toughness, and can produce a ____________
microstructure
heat to desired temperature, hold (soak) at this temperature, cool to room
temperature Correct Answer: steps of annealing
process annealing Correct Answer: negate the effects of cold work and softened
and increases the ductility of a strain-hardened metal (recovery and
recrystallization)
stress relief Correct Answer: heat treatment to remove residual stress
plastic deformation (i.e. machining), non-uniform cooling after processing at an
elevated temperature (i.e. welding and casting), and phase transformations induced
on cooling (i.e. martensite) Correct Answer: internal stresses can develop with...
stress relief annealing heat treatment Correct Answer: component heated to
recommended low temperature, held at this uniform temperature, and cooled to
room temperature in air
normalizing Correct Answer: refines grains and produces a more uniform and
desirable size distribution (at least 55°C above upper critical temperature),
transformed to austenite, then cooled in air
full annealing Correct Answer: heat treatment in low to medium carbon steels to
produce coarse pearlite in components that will be machined or experience
extensive plastic deformation
spheroidizing Correct Answer: carried out a temperature just below the eutectoid
in which the spheroidite microstructure is produced
The benefits of buying summaries with Stuvia:
Guaranteed quality through customer reviews
Stuvia customers have reviewed more than 700,000 summaries. This how you know that you are buying the best documents.
Quick and easy check-out
You can quickly pay through EFT, credit card or Stuvia-credit for the summaries. There is no membership needed.
Focus on what matters
Your fellow students write the study notes themselves, which is why the documents are always reliable and up-to-date. This ensures you quickly get to the core!
Frequently asked questions
What do I get when I buy this document?
You get a PDF, available immediately after your purchase. The purchased document is accessible anytime, anywhere and indefinitely through your profile.
Satisfaction guarantee: how does it work?
Our satisfaction guarantee ensures that you always find a study document that suits you well. You fill out a form, and our customer service team takes care of the rest.
Who am I buying this summary from?
Stuvia is a marketplace, so you are not buying this document from us, but from seller Classroom. Stuvia facilitates payment to the seller.
Will I be stuck with a subscription?
No, you only buy this summary for R184,78. You're not tied to anything after your purchase.