MECH221 Assignment mid #7 –Concordia University9.11 Is it possible to have a copper–silver alloy that, at equilibrium, consists of a β phase of composition 92 wt%
Ag–8 wt% Cu and also a liquid phase of composition 76 wt% Ag–24 wt% Cu? If so, what will be the approximate
temperature of the alloy? If this is not possible, explain why.
Solution
It is possible to have a Cu-Ag alloy, which at equilibrium consists of a phase of composition 92 wt% Ag-
8 wt% Cu and a liquid phase of composition 77 wt% Ag-23 wt% Cu. From Figure 9.7 a horizontal tie line can be
constructed across the + L phase region at about 800 C which intersects the L–( + L) phase boundary at 76 wt%
Ag, and also the ( + L)– phase boundary at 92 wt% Ag.
9.13 A lead–tin alloy of composition 30 wt% Sn–70 wt% Pb is slowly heated from a temperature of 150°C (300°F).
(a) At what temperature does the first liquid phase form?
(b) What is the composition of this liquid phase?
(c) At what temperature does complete melting of the alloy occur?
(d) What is the composition of the last solid remaining prior to complete melting?
Solution
Upon heating a lead-tin alloy of composition 30 wt% Sn-70 wt% Pb from 150 C and utilizing Figure 10.8
as shown below:
Page 1 of 18
, (a) The first liquid forms at the temperature at which a vertical line at this composition intersects
the eutectic isotherm--i.e., at 183 C.
Page 2 of 18
, (b) The composition of this liquid phase corresponds to the intersection with the ( + L)–L phase
boundary, of a tie line constructed across the + L phase region just above this eutectic isotherm--i.e., CL = 61.9
wt% Sn.
(c) Complete melting of the alloy occurs at the intersection of this same vertical line at 30 wt% Sn with
the ( + L)–L phase boundary--i.e., at about 260 C.
(d) The composition of the last solid remaining prior to complete melting corresponds to the intersection
with –( + L) phase boundary, of the tie line constructed across the + L phase region at 260 C--i.e., C is about
13 wt% Sn.
9.16 For an alloy of composition 52 wt% Zn–48 wt% Cu, cite the phases present and their mass fractions at the
following temperatures: 1000°C, 800°C, 500°C, and 300°C.
Solution
This problem asks us to determine the phases present and their concentrations at several temperatures,
as an alloy of composition 52 wt% Zn-48 wt% Cu is cooled. From Figure 9.19 (the Cu-Zn phase diagram), which is
shown below with a vertical line constructed at the specified composition:
At 1000 C, a liquid phase is present; WL = 1.0
At 800 C, the phase is present, and W = 1.0
At 500 C, and phases are present, and from the tie lie constructed on the above diagram
Page 3 of 18
Dit zijn jouw voordelen als je samenvattingen koopt bij Stuvia:
Bewezen kwaliteit door reviews
Studenten hebben al meer dan 850.000 samenvattingen beoordeeld. Zo weet jij zeker dat je de beste keuze maakt!
In een paar klikken geregeld
Geen gedoe — betaal gewoon eenmalig met iDeal, Bancontact of creditcard en je bent klaar. Geen abonnement nodig.
Focus op de essentie
Studenten maken samenvattingen voor studenten. Dat betekent: actuele inhoud waar jij écht wat aan hebt. Geen overbodige details!
Veelgestelde vragen
Wat krijg ik als ik dit document koop?
Je krijgt een PDF, die direct beschikbaar is na je aankoop. Het gekochte document is altijd, overal en oneindig toegankelijk via je profiel.
Tevredenheidsgarantie: hoe werkt dat?
Onze tevredenheidsgarantie zorgt ervoor dat je altijd een studiedocument vindt dat goed bij je past. Je vult een formulier in en onze klantenservice regelt de rest.
Van wie koop ik deze samenvatting?
Stuvia is een marktplaats, je koop dit document dus niet van ons, maar van verkoper smartzone. Stuvia faciliteert de betaling aan de verkoper.
Zit ik meteen vast aan een abonnement?
Nee, je koopt alleen deze samenvatting voor €11,27. Je zit daarna nergens aan vast.
Is Stuvia te vertrouwen?
4,6 sterren op Google & Trustpilot (+1000 reviews)
Afgelopen 30 dagen zijn er 69052 samenvattingen verkocht
Opgericht in 2010, al 15 jaar dé plek om samenvattingen te kopen